Lencaqi L-180 Polymer Waterproofing Coating(Permeable Crystallization Type)

Introduction:

This product is by the German basf, high-performance synthetic acrylate polymer emulsion and inorganic powder according to the proportion of science into a two-component products . Has good permeability, corrosion and bonding performance.

Features:

1. Excellent bonding performance

2. Be used on damp base

3. Corrosion resistance, high temperature resistant, low temperature resistance, ageing resistance

4. Non-toxic, harmless, tasteless, no pollute the environment

5. Permeable crystallization waterproof,If no artificial damage and structural deformation, with buildings same life.

6. Especially suitable for directly paste veneer material on the waterproof layer(Such as putty, sand ash, ceramic tile, etc)

Range of application:

1. Especially suitable for families which need attach with ceramic tile of toilet, kitchen, close balcony, moisture of water proof and seepage proof.Can also be used for the construction with waterproof, anti-corrosion

2. Industrial and civil construction of seepage prevention and seepage repair,waterproof, seepage prevention of all kinds of pools and swimming pool.

3. Aerated concrete surface sealed and waterproof, seepage control, As interface treatment agent

4. Repair of the highway bridge engineering

5. Polystyrene insulation board and ceramic tile’s adhesive, With anti-corrosion, waterproof function.

Construction tips:

(1) Base surface must be firm, smooth, no dust, no pollution, no cast and other

(2) Base surface voids, holes, cracks, etc with Lencaqi’s quick Condensing Plugging king filling wall and smooth, sharp edges and bump should be removed.

(3) Bases are required to be humid before construction.( But can't have hydrops) The basal application of porous type with delayed coagulation Plugging king smooth, internal and external corner and other node do circular arc Angle(internal corner R>50mm,external cornerR>10mm).

Method of application:

(1). Pour powders into matched emulsion slowly and keep stirring until the lump of solid in the mixture disappear. Stop stirring for 10min and stir for 2min before use. Better to keep stirrer at the bottom of the container in case of air introduction. The mixed products should be used within 1 hour.

(2). Paint the mixture on humid but ponding-free base uniformly with palm fibre brush. Every layer should not be constructed before previous layer is solidified and each layer should be brushed inperpendicular direction to previous layer. Wool brush is suggested for the last layer to get smoother surface. If this is a finish coat layer, it is suggested to do crosswise drawbench treatment with palm fibre brush to enhance adhesive property.(all thickness is 1.5-2mm)

(3). Fiberglass cloth can be used in large crack or deformation joint. High pressure spraying method is suggested in large area construction.

Notes:

1. Construction temperature : 5 - 35°C

2. Construction under sun exposure should be prevented in summer

3. After Construction was finished 24 hours should be sprinkler maintenance 2-3 days

4. Tear after packing should be used up in a short time, should not be stored for a long time

Reference dosage:

1. Applying for dampproof, reference dosage is 1.2 kg/m2, one layer of brush work about 0.7mm thick on smooth base.

2. Applying for waterproof, twice brushworks of 2.5-3.5 kg/m2 are recommended to obtain 1.5-2mm thickness. Specific amount depending on the base status.

Technical parameters: