Product Description

HY Series Water-Borne Bentonite Rheological Additive

HY series water-based bentonite Theological additives (inorganic gel) is a kind of natural aluminum,magnesium silicate, rheological additives. It is a purificalion of modified montmorillonite clay with the features of gray-white, non-toxic, tasteless, soft texture powder, the main ingredient for the product is hydrophilic, high-purity (modified) montmorillonite, its colloidal system is similar to Vanderbilt and Colloid Company's Veegum or Magnabrite products. With excellent swellability in water, colloidaldispersion, suspensien, thickening and thixotropy, it is the excellent anti-settling agent, emulsion stabilizers and rheological additives for water-based system, and further it has good adsorption, ion exchangeability, non-migration adhesion, etc. In some areas, it is becoming an excellent assistant new type of alternative materials.

Applied Industries	Functions
Waterborne coatings,inks,latex paint,rubber,paper,diatom mud,pesticides	Used as a thixotropic agent for suspension and paste, a emulsion stabilizers,thickeners
The pharmaceutical industry, the feed industry,cosmetics,toothpaste	Used as a drug binder and stabiizer;feed additives; a thixotropic agent, thickener and stabilizer for emulsion
Specoalty foundry coating, cement mortar and a variety of ceramic glaze paint	Used as a suspending, thixotropic agent for the base material

The performance of the products in many respects are superior to separate organic polymer such as CMC, HEC.

Main Products:HY-30C, HY-30E, HY-30EV, HY-EW-2, HY-30 lithium-based
The product has the following characteristics:
1. Strong thixotropy: high shear with low viscosity, low shear with high viscosity, thixotropic index is 6.0
2. Wide PH range: within PH5-12 play a thickening function.
3. Easy dispersion: without process for the preparation of the pre-gel, without a polar activator.
4. Stability: superior biochemistry stability, goad thermal stability.
5. Compatibility: good compatibility with alcohols and highly polar solvents [such as glycerin, sorbitol).
6. Economical Efficiency: it will reduce the cost when using the product alone.Mixed with the cellulose aether,acrylic acid will improve the rhealogical property,and reduce the costs at the same time!

HY Series bentonite rheological additives( inorganic gel) quality indicators

Products	Appearance	Whiteness	PH Value	Surface Viscosity	Heavy metal content (PPM)			Montmorillonite content(%)≥
					Pb	As	Hg
HY-30C	Gray Powder	>75	6.5-10.5	>250	<10	<0.3	<0.1	80
HY-30E	Gray Powder	>75	6.5-10.5	>200				85
HY-30EV	Gray Powder	>75	6.5-10.5	>500				85
HY-EW-2	Gray Powder	>80	6.5-10.5	>800				90
HY-30 lithium-based	Gray Powder	>80	6.5-10.5	>200				85

Attention: Recommended viscosity test method: al the temperature of 25°C, make a pre-gel (the amount of bentaniie }s 50% of the whole system) stand it for 60 minutes, test the viscosily wcth a Brookfield DV II viscometer with the rotor #6,100r/min.!

Main chemical ingredients(%)

SiO2	Al2O3	MgO	TiO2	Fe2O3	CaO	K2O	Na2O
60-62	19-20	3.89-4.40	<0.01	1.0-1.5	2.0-3.0	0.25-0.35	0.1-0.2

Use method:

(1)pre-gel method:
The HY series bentonite (inorganic gel) rheological additives could be used as pre-gel:The preparation of a pre-gel concentration should be decided according to the desired viscosity level of the stirring speed and the product of the dispersing device in order to obtain the best results.Generally
speaking, 2-10% (mass percentage of the whole system).Weigh a certain amount of the product under stirring slowly added to water of 25- 30°C Note avoid caking. After the addition, adjust the speed to 1000-1200RPM, and disperse it by stirring for 30 minutes, so that products can sufficiently dispersed into the water and form a uniform gel, stand it for 8-24 hours, and use it after the colloidal plays stabilized thickening effect.
(2] Dry pawder method:
HY Series bentonite rheological additives (inorganic gel) can be directly put into required system as dry powder.Formulated concentration of the system should be decided according to the needs of the various indicators of the stirring speed and the dispersing device (viscosity level, thixotropy, etc.) in.

Note:

(1)HY series inorganic gel will take effect under the condition of dispersing enough.It will increase the function of thickening, anti settling,thixortapy of the gel is proper stored Surface activator,diatomic alcohol will disturb the hydration,it should be added after HY Series
dispersed mouth!
(2)HY series in organic gel can be used alone or mixing with thickening agent such as carboxyrnethyl cellulose,hydroxy ethyl cell close,CMHPC,which will acquire best rheological property.It has been found that this kind of product should avoid mixing with the polyurethane thickening agent.

Packaging & Shipping

Package and storage:

The package consists of external package(kraft paper bag)and internal package(polyethylene film bag).The value bag is also available and the weight is usually 25 ± 0.25Kg.The package can also be customized. If stored in dry place and kept packaged(at the temperature of 0°C-3 0 °C),the organic bentonite is effective within 36 months.